wlft404_405_.jpg
suitable for blanks
  • specific thermal resistance: 3.7°C cm2/W
  • temperature range: -30°C... +125°C
  • holding force (overlapping): 0.86 MPa
  • holding force (shear force):
    • Al 25°C 0.897 [MPa]

    • Al
      150°C 0.345 [MPa]

    • Cu
      25°C 0.828 [MPa]

    • Cu
      150°C 0.31 [MPa]

    • Al
      2O3 25°C 1.17 [MPa]

    • Al
      2O3 150°C 0.34 [MPa]
wlft404_405_.jpg
suitable for blanks
  • specific thermal resistance: 3.7°C cm2/W
  • temperature range: -30°C... +125°C
  • holding force (overlapping): 0.86 MPa
  • holding force (shear force):
    • Al 25°C 0.897 [MPa]

    • Al
      150°C 0.345 [MPa]

    • Cu
      25°C 0.828 [MPa]

    • Cu
      150°C 0.31 [MPa]

    • Al
      2O3 25°C 1.17 [MPa]

    • Al
      2O3 150°C 0.34 [MPa]
wlft404_405_.jpg
suitable for blanks
  • specific thermal resistance: 3.7°C cm2/W
  • temperature range: -30°C... +125°C
  • holding force (overlapping): 0.86 MPa
  • holding force (shear force):
    • Al 25°C 0.897 [MPa]

    • Al
      150°C 0.345 [MPa]

    • Cu
      25°C 0.828 [MPa]

    • Cu
      150°C 0.31 [MPa]

    • Al
      2O3 25°C 1.17 [MPa]

    • Al
      2O3 150°C 0.34 [MPa]
wlft404_405_.jpg
suitable for blanks
  • specific thermal resistance: 3.7°C cm2/W
  • temperature range: -30°C... +125°C
  • holding force (overlapping): 0.86 MPa
  • holding force (shear force):
    • Al 25°C 0.897 [MPa]

    • Al
      150°C 0.345 [MPa]

    • Cu
      25°C 0.828 [MPa]

    • Cu
      150°C 0.31 [MPa]

    • Al
      2O3 25°C 1.17 [MPa]

    • Al
      2O3 150°C 0.34 [MPa]
wlft404_405_.jpg
suitable for blanks
  • specific thermal resistance: 3.7°C cm2/W
  • temperature range: -30°C... +125°C
  • holding force (overlapping): 0.69 MPa
  • holding force (shear force):
    • Al 25°C 1.04 [MPa]

    • Al
      150°C 0.104 [MPa]
wlft404_405_.jpg
suitable for blanks
  • specific thermal resistance: 3.7°C cm2/W
  • temperature range: -30°C... +125°C
  • holding force (overlapping): 0.69 MPa
  • holding force (shear force):
    • Al 25°C 1.04 [MPa]

    • Al
      150°C 0.104 [MPa]
wlft404_405_.jpg
suitable for blanks
  • specific thermal resistance: 3.7°C cm2/W
  • temperature range: -30°C... +125°C
  • holding force (overlapping): 0.69 MPa
  • holding force (shear force):
    • Al 25°C 1.04 [MPa]

    • Al
      150°C 0.104 [MPa]
wlft404_405_.jpg
suitable for blanks
  • specific thermal resistance: 3.7°C cm2/W
  • temperature range: -30°C... +125°C
  • holding force (overlapping): 0.69 MPa
  • holding force (shear force):
    • Al 25°C 1.04 [MPa]

    • Al
      150°C 0.104 [MPa]
wlft404_405_.jpg
suitable for blanks
  • specific thermal resistance: 3.4°C cm2/W
  • temperature range: -30°C... +125°C
  • holding force (overlapping): 0.93 MPa
  • holding force (shear force):
    • Al 25°C 0.86 [MPa]

    • Al
      150°C 0.38 [MPa]

    • Cu
      25°C 1.1 [MPa]

    • Cu
      150°C 0.48 [MPa]

    • Al
      2O3 25°C 1.0 [MPa]

    • Al
      2O3 150°C 0.41 [MPa]
wlft404_405_.jpg
suitable for blanks
  • specific thermal resistance: 3.4°C cm2/W
  • temperature range: -30°C... +125°C
  • holding force (overlapping): 0.93 MPa
  • holding force (shear force):
    • Al 25°C 0.86 [MPa]

    • Al
      150°C 0.38 [MPa]

    • Cu
      25°C 1.1 [MPa]

    • Cu
      150°C 0.48 [MPa]

    • Al
      2O3 25°C 1.0 [MPa]

    • Al
      2O3 150°C 0.41 [MPa]
wlft404_405_.jpg
suitable for blanks
  • specific thermal resistance: 3.4°C cm2/W
  • temperature range: -30°C... +125°C
  • holding force (overlapping): 0.93 MPa
  • holding force (shear force):
    • Al 25°C 0.86 [MPa]

    • Al
      150°C 0.38 [MPa]

    • Cu
      25°C 1.1 [MPa]

    • Cu
      150°C 0.48 [MPa]

    • Al
      2O3 25°C 1.0 [MPa]

    • Al
      2O3 150°C 0.41 [MPa]
wlft404_405_.jpg
suitable for blanks
  • specific thermal resistance: 3.4°C cm2/W
  • temperature range: -30°C... +125°C
  • holding force (overlapping): 0.93 MPa
  • holding force (shear force):
    • Al 25°C 0.86 [MPa]

    • Al
      150°C 0.38 [MPa]

    • Cu
      25°C 1.1 [MPa]

    • Cu
      150°C 0.48 [MPa]

    • Al
      2O3 25°C 1.0 [MPa]

    • Al
      2O3 150°C 0.41 [MPa]